The work presents the results of the research and tests of the surface machining of the S355NL and X5CrNi18-10 steels with the concentraded stream of heat with the usage of the GTAW method. The surface layers of the tested steels were remelted with the electric arc using the current of the electric arc 50, 100, 150 and 200A.The machining was done in the atmosphere of argon with the constant speed of the welding head. A microscope examination was performed of the obtained structure and measurements of depth, width and hardness of the received surface layer were performed. Moreover the relation between the current of the electric arc and geometry of the remelted layers with their microhardness was examined.
Przejdź do artykułu

Abstrakt

The aim of that work was the evaluation of the quality of welded connections elements (welds) from the 30HGS steel and titanium alloy Ti6Al4V. The metallographic, factographic tests were used, and measurements of microhardness with the Vickers method. In the head weld of the 30HGS steel there were non-metallic partial division and bubbles observed. The average microhardness in the head connection was 320 HV0.1. There was no significant increase/decrease observed of microhardness in the head influence zone of the weld. There was a good condition of head connections observed, in accordance with the standard EN12517 and EN25817. In the head weld of Ti6Al4V titanium alloy there were single, occasional non-metallic interjections and bubbles observed. There were no cracks both on the weld, and on the border of the heat influence zone. The value of microhardness in head connection was in the range 300÷445 HV0.1. Reveal a very good condition of the head connections in accordance with the standard EN12517 and EN25817. The factographic tests prove the correctness of welded connections done and then heat treatment in case of steel and titanium alloy.
Przejdź do artykułu

Ta strona wykorzystuje pliki 'cookies'. Więcej informacji