Metallographic investigations and a computer simulation of stresses in a gravity die-casting bushing were performed. Simulation of the casting process, solidification of the thick-walled bushing and calculations of the stress was performed using MAGMA5.3 software. The size variability of phases κIIaffecting the formation of phase stresses σf, depending on the location of the metallographic test area, was identified. The distribution of thermal σtand shrinkage stresses σs, depending on the location of the control point SC in the bushing's volume, was estimated. Probably the nature of these stresses will change slightly even after machining. This can cause variations in operating characteristics (friction coefficient, wear). Due to the strong inhomogeneity of the stress distribution in the bushing's casting, it is necessary to perform further tests of the possibility to conduct thermal treatment guaranteeing homogenization of the internal stresses in the casting, as well as to introduce changes in the bushing's construction and the casting technology. The paper presents the continuation of the results of research aimed at identifying the causes of defects in the thick-walled bushing, die-casting made of CuAl10Fe5Ni5Cr aluminium bronze.
Go to article

Abstract

For the die casting conditions of aluminium bronzes assumed based on the literature data, a thick-walled bush was cast, made of complex aluminium bronze (Cu-Al-Fe-Ni-Cr). After the cast was removed from the mould, cracks were observed inside it. In order to identify the stage in the technological production process at which, potentially, the formation of stresses damaging the continuity of the microstructure created in the cast was possible (hot cracking and/or cold cracking), a computer simulation was performed. The article presents the results of the computer simulation of the process of casting the material into the gravity die as well as solidifying and cooling of the cast in the shape of a thick-walled bush. The simulation was performed with the use of the MAGMA5 program and by application of the CuAl10Ni5,5Fe4,5 alloy from the MAGMA5 program database. The results were compared with the location of the defects identified in the actual cast. As a result of the simulation of the die-casting process of this bush, potential regions were identified where significant principal stresses accumulate, which can cause local hot and cold cracking. Until now, no research has been made of die-cast aluminium bronzes with a Cr addition. Correlating the results of the computer simulation validated by the analysis of the actual cast made it possible to clearly determine the critical regions in the cast exposed to cracking and point to the causes of its occurrence. Proposals of changes in the bush die casting process were elaborated, in order to avoid hot tearing and cold cracking. The article discusses the results of preliminary tests being a prologue to the optimization of the die-casting process parameters of complex aluminium bronze thick-walled bushs.
Go to article

Abstract

The article presents the investigations of 7xxx aluminium alloys performed by the method of thermal and derivational analysis. The studies made it possible to identify the effect of the changes in the Cu concentration, the total Zn and Mg weight concentrations and the Zn/Mg weight concentration ratio on their crystallization process: the cooling as well as the kinetics and dynamics of the thermal process of cooling and crystallization. Metallographic studies were performed on the microstructure of the examined alloys and their HB hardness was measured. The evaluation of the changes was presented in reference to the model alloys EN AW-7003 and EN AW-7010, whose microstructure under the conditions of thermodynamic equilibrium are described by the phase diagrams: Al-Zn-Mg and Al-Zn-Mg-Cu. The performed investigations confirmed that the hardness HB of the examined alloys is mainly determined by the reinforcement of the matrix αAl by the introduced alloy additions and the presence of phases Θ(Al2Cu) and S(Al2CuMg) rich in copper, as well as η(MgZn2), in the examined alloys' microstructure. The increase of the amount of intermetallic phases precipitated in the microstructure of the examined alloys is caused, beside Cu, by the characteristic change of Zn wt. concentration and Mg. It was proposed that the process of one-stage thermal treatment of the examined alloys be introduced at a temperature of up to tJ-20 °C, which will prevent the exceedance of the solidus temperature.
Go to article

Abstract

The study presents the results of the investigations of the effect of Cu, Ni, Cr, V, Mo and W alloy additions on the microstructure and mechanical properties of the AlSi7Mg0.3 alloy. The examinations were performed within a project the aim of which is to elaborate an experimental and industrial technology of producing elements of machines and devices complex in their construction, made of aluminium alloys by the method of precision investment casting. It was demonstrated that a proper combination of alloy additions causes the crystallization of complex intermetallic phases in the silumin, shortens the SDAS and improves the strength properties: Rm, Rp0.2,HB hardness. Elevating these properties reduces At, which, in consequence, lowers the quality index Q of the alloy of the obtained casts. Experimental casts were made in ceramic moulds preliminarily heated to 160 °C, into which the AlSi7Mg0.3 alloy with the additions was cast, followed by its cooling at ambient temperature. With the purpose of increasing the value of the quality index Q, it is recommended that the process of alloy cooling in the ceramic mould be intensified and/or a thermal treatment of the casts be performed (ageing)(T6).
Go to article

Abstract

The work presents the results of the investigations of the effect of inhibitors coated on the internal walls of a ceramic mould on the quality of the obtained casts made of the AM60 alloy containing additions of chromium and vanadium. In order to reduce the reactivity of magnesium alloy cast by the technology of investment casting with the material of the mould and the ambient atmosphere, solid inhibitors were applied in the form of a mixture of KBF4 and H3BO3 after the stage of mould baking and before the mould’s being filled with the liquid alloy. For the purpose of examining the effect of the inhibitors on the surface quality of the obtained casts, profilometric tests were performed and the basic parameters describing the surface roughness, Ra, Rz and Rm, were determined.
Go to article

Abstract

The article presents the investigation results of the crystallization (performed by means of the TDA method) and the microstructure of complex aluminium bronzes with the content of 6% Al, 4% Fe and 4% Ni, as well as Si additions in the scope of 1–2% and Cr additions in the scope of 0.1–0.3%, which have not been simultaneously applied before. For the examined bronze, the following tests were performed: hardness HB, impact strength (KU2). For bronze CuAl6Fe4Ni4Si2Cr0.3, characterizing in the highest hardness, wear tests were conducted with dry friction and the dry friction coefficient. The investigations carried out by means of the X-ray phase analysis demonstrated the following phases in the microstructure of this bronze: αCu, γ2 and complex intermetallic phases based on iron silicide type Fe3Si (M3Si M={Fe,Cr,…}). Compared to the normalized aluminium bronzes (μ=0.18–0.23), the examined bronze characterizes in relatively low wear and lower friction coefficient during dry friction (μ=0.147±0.016).