The paper presents the results of the electrodeposition of nickel composite coatings reinforced with the ceramic SiC particles. A Watts type galvanic bath modified with various organic additives was used. These additives were: 2-sulfobenzoic acid imide (LSA), dioctyl sulfosuccinate sodium salt (DSS), sodium dodecyl sulfate (SDS), tris (hydroxymethyl) aminomethane (THAM) and hexamethyldisilizane (HMDS). The nickel composite coating was electrodeposited on a 2xxx aluminum alloy series substrate (EN-AW 2017) with zinc interlayer. Studies concerned the effect of the applied organic additives on properties of composite coatings such as: microstructure, microhardness, adhesion to the substrate, corrosion resistance and roughness. The structure of the coatings was assessed by scanning electron microscopy and light microscopy. Based on the studies of zeta potential it was found that the bath modification had a significant impact on the amount of the ceramic phase embedded in metal matrix. The tests conducted in a model 0.01 M KCl solution were not fully representative of the true behavior of particles in a Watts bath.
Go to article

Abstract

The effect of plastic deformation process on the dissolution rate of biocompatible Mg alloys was investigated. Two biocompatible MgLi1Ca0,2Zn1 and MgLi1Ca1Zn1 alloys were selected for the study. The alloys were deformed on a 100T press at a temperature of 350°C by conventional extrusion and by the equal channel angular extrusion process (ECAE). The grain size analysis showed a high degree of the grain refinement from approximately 110 mm in the initial state to 2.8 mm after the 3rd pass of the ECAE process. Compared to as-cast state, the degree of strengthening has increased after plastic forming. The results of biodegradation tests have shown a significant increase in corrosion rate after both conventional extrusion and ECAE, although after subsequent ECAE passes, this rate was observed to slightly decrease in the MgLi1Ca1Zn1 alloy. Based on the results of macro- and microstructure examinations, the corrosion progress in samples after the extrusion process was described.
Go to article

This page uses 'cookies'. Learn more