Ductile irons of the type of Si-Mo are characterized by increased resistance to long-term influence of high temperatures and cyclic temperature changes. They are mainly used in castings of combustion engine exhaust piping and other castings utilized at temperatures of up to 850°C. The aim of the study is to verify the mechanical properties of non-alloyed cast iron EN CSN GJS 450, SiMo4-0.5 and SiMo5-1 ductile irons at temperatures of 700 to 800°C, and the extent of their superficial oxidation after longterm annealing at a temperature of 900°C. Via chemical microanalysis the composition of oxidation products in the surface layer was evaluated.
At thermal junctions of aluminium alloy castings and at points where risering proves to be difficult there appear internal or external shrinkages, which are both functionally and aesthetically inadmissible. Applying the Probat Fluss Mikro 100 agent, which is based on nano-oxides of aluminium, results in the appearance of a large amount of fine microscopic pores, which compensate for the shrinking of metal. Experimental tests with gravity die casting of AlSi8Cu3 and AlSi10Mg alloys have confirmed that the effect of the agent can be of advantage in foundry practice, leading to the production of castings without local concentrations of defects and without the appearance of shrinkages and macroscopic gas pores. Also, beneficial effect on the mechanical properties of the metal has been observed.