A nanocrystalline Ti alloy powder was fabricated using cryomilling. The grain size and lattice strain evolution during cryomilling were quantitatively analyzed using X-ray diffraction (XRD) based on the Scherrer equation, Williamson-Hall (W-H) plotting method, and size-strain (S-S) method assuming uniform deformation. Other physical parameters including stress and strain have been calculated. The average crystallite size and the lattice strain evaluated from XRD analysis are in good agreement with the result of transmission electron microscopy (TEM).
In this study, the combined effect of Zr and Si on isothermal oxidation of Ti for 25 and 50 h at 820°C, which is the temperature related to exhaust valves operation, was investigated. Si addition into Ti-5mass%Zr alloy led to a distribution of silicide Ti5Si3 phase formed by a eutectic reaction. The Ti sample containing only Zr showed more retarded oxidation rate than Ti-6Al-4V, the most prevalent Ti alloy, at the same condition. However, while a simultaneous addition of Zr and Si resulted in greater increase of oxidation resistance. The oxide layer formed after the addition of Zr and Si comprised TiO2, ZrO2, and SiO2.
This study attempted to manufacture an Y2O3 ceramic coating layer on a ceramic (AlN) substrate using aerosol deposition (AD) and investigated its macroscopic properties. Pure Y2O3 powder with a polygonal shape and average size of 5.0 μm was used as initial feedstock. Using aerosol deposition with suitable process conditions, an Y2O3 coating layer was successfully fabricated on aluminum nitride (AIN). The thickness of the manufactured coating layer was approximately 10 mm. The coating layer consisted of Y2O3 phase identical to that in the initial powder, and no additional oxides were identified. In regard to the roughness of the Y2O3 coating layer, the average roughness (Ra) measured 1.32 μm, indicating that the surface roughness was relatively even compared to the initial powder size (5 μm). Mechanical properties of the Y2O3 coating layer were measured using nano indentation equipment, and the indentation modulus of the Y2O3 coating layer fabricated by aerosol deposition measured 136.5 GPa. The interface of the coating layer was observed using TEM, and the deposition mechanism of the Y2O3 coating layer manufactured by aerosol deposition was also discussed.
Fe-Cr-B alloy is a material with precipitation of boride inside Fe matrix, and it features outstanding hardness and wear resistance properties. However, Fe-Cr-B alloy is a difficult material to process, making it difficult to use as a bulk type structure material which requires delicate shapes. This study attempted to manufacture Fe-Cr-B alloy using a 3D printing process, laser metal deposition. This study also investigated the microstructure, hardness and compression properties of the manufactured alloy. Phase analysis results is confirmed that α-Fe phase as matrix and (Cr, Fe)2B phase as reinforcement phase. In the case of (Cr, Fe)2B phase, differences were observed according to the sample location. While long, coarse, unidirectional needle-type boride phases (~11 μm thickness) were observed in the center area of the sample, relatively finer boride phases (~6 μm thickness) in random directions were observed in other areas. At room temperature compression test results confirmed that the sample had a compression strength is approximately 2.1 GPa, proving that the sample is a material with extremely high strength. Observation of the compression fracture surface identified intergranular fractures in areas with needle-type boride, and transgranular fractures in areas with random borides. Based on this results, this study also reviewed the deformation behavior of LMD Fe-Cr-B alloy in relation to its microstructures.