Tests concerning EN AC 48000 (AlSi12CuNiMg) alloy phase transition covered (ATD) thermal analysis and (DSC) differential scanning calorimetry specifying characteristic temperatures and enthalpy of transformations. ATD thermal analysis shows that during cooling there exist: pre-eutectic crystallization effect of Al9Fe2Si phase, double eutectic and crystallization α(Al)+β(Si) and multi-component eutectic crystallization. During heating, DSC curve showed endothermic effect connected with melting of the eutectic α(Al)+β(Si) and phases: Al2Cu, Al3Ni, Mg2Si and Al9Fe2Si being its components. The enthalpy of this transformation constitutes approx. +392 J g-1 . During freezing of the alloy, DSC curve showed two exothermal reactions. One is most likely connected with crystallization of Al9Fe2Si phase and the second one comes from freezing of the eutectic α(Al)+β(Si). The enthalpy of this transformation constitutes approx. –340 J g-1 . Calorimetric test was accompanied by structural test (SEM) conducted with the use of optical microscope Reichert and scanning microscope Hitachi S-4200. There occurred solution's dendrites α(Al), eutectic silicon crystal (β) and two types of eutectic solution: double eutectic α(Al)+β(Si) and multi-component eutectic α+AlSiCuNiMg+β.
With the use of differential scanning calorimetry (DSC), the characteristic temperatures and enthalpy of phase transformations were defined for commercial AlSi9Cu3 cast alloy (EN AC-46000) that is being used for example for pressurized castings for automotive industry. During the heating with the speed of 10oCmin-1 two endothermic effects has been observed. The first appears at the temperature between 495 oC and 534 oC, and the other between 555 oC and 631 oC. With these reactions the phase transformation enthalpy comes up as +6 J g-1 and +327 J g-1 . During the cooling with the same speed, three endothermic reactions were observed at the temperatures between 584 oC and 471 oC. The total enthalpy of the transitions is – 348 J g-1 . Complimentary to the calorimetric research, the structural tests (SEM and EDX) were conducted on light microscope Reichert and on scanning microscope Hitachi S-4200. As it comes out of that, there are dendrites in the structure of α(Al) solution, as well as the eutectic (β) silicon crystals, and two types of eutectic mixture: double eutectic α(Al)+β(Si) and compound eutectic α+Al2Cu+β.
The paper presents results of calorimetric studies of foundry nickel superalloys: IN100, IN713C, Mar - M247 and ŻS6 U. Particular attention was paid to determination of phase transiti ons temperatures during heating and cooling. The samples were heated to a temperature of 1500°C with a rate of 10°C ⋅ min – 1 and then held at this temperature for 5 min. After a complete melting, the samples were cooled with the same rat e. Argon with a purity of 99.99% constituted the protective atmosphere. The sample was placed in an alundum crucible with a capacity of 0.45 cm 3 . Temperature and heat calibration was carried out based on the mel ting point of high- purity Ni. The tests were carried out by the differential scanning calorimetry (DSC) using a Multi HTC high -temperature calorimeter from Setaram. Based on the DSC curves, the following temperatures were determined: solidus and liquidus, dissolution and precipitation of the γ ’ phase, MC carbides and melting of the γ ’ /γ eutectic. In the temperature range of 100 -1100°C, specific heat capacity of the investigated superalloys was determined. It was found that the IN713C and IN100 alloys exhibit a higher specific heat while compared to the Mar - M247 and ŻS6 U alloys.