In this paper is discussed the effect of the inoculant mischmetal addition on the microstructure of the magnesium alloy AZ91. The concentration of the inoculant was increased in the samples within the range from 0.1% up to 0.6%. The thermal process was performed with the use of Derivative and Thermal Analysis (DTA). A particular attention was paid to finding the optimal amount of the inoculant, which causes fragmentation of the microstructure. The concentration of each element was verified with use of a spark spectrometer. In addition, the microstructures of every samples were examined with the use of an optical microscope and also was performed an image analysis with a statistical analysis using the NIS–Elements program. The point of those analyses was to examine the differences in the grain diameters of phase αMg and eutectic αMg+γ(Mg17Al12) in the prepared samples as well as the average size of each type of grain by way of measuring their perimeters. This paper is the second part of the introduction into a bigger research on grain refinement of magnesium alloys, especially AZ91. Another purpose of this research is to achieve better microstructure fragmentation of magnesium alloys without the relevant changes of the chemical composition, which should improve the mechanical properties.
This paper presents the results of Cr - Ni 18/9 austenitic cast steel modifications by mischmetal. The study was conducted on industrial melts. Cast steel was melted in an electric induction furnace with a capacity of 2000 kg and a basic lining crucible. .The mischmetal was introduced into the ladle during tapping of the cast steel from the furnace. The effectiveness of modification was examined with the carbon content of 0.1% and the presence of δ ferrite in the structure of cast steel stabilized with titanium. The changes in the structure of cast steel and their effect on mechanical properties and intergranular corrosion were studied. It was found that rare earth metals decrease the sulfur content in cast steel and above all, they cause a distinct change in morphology of the δ ferrite and non-metallic inclusions. These changes have improved mechanical properties. R02, Rm, and A5 and toughness increased significantly. There was a great increase of the resistance to intergranular corrosion in the Huey test. The study confirmed the high efficiency of cast steel modification by mischmetal in industrial environments. The final effect of modification depends on the form and manner of placing mischmetal into the liquid metal and the melting technology, ie the degree of deoxidation and desulfurization of the metal in the furnace.