Abstract

This paper shows results of researches of a structure and mechanical properties of metal sheets of IF steels subjected torecrystallization annealing. The annealing was held in the scope of the temperature of 600-900°C over 25 min time. The impact of heat treatment on changes of properties and structure of the researches steel has been analysed. During annealing typical processes of rebuilding of the structure deformed as a result of cold deformation in the form of forming new recrystallized grains and their growth were observed. As the temperature of annealing increases the hardness of the material gradually decreases.
Go to article

Abstract

This paper presents results obtained from a laboratory investigation conducted on material from a pressure vessel after longterm operation in the oil refinery industry. The tested material contained structural defects which arose from improper heat treatment during steel plate manufacturing. Complex tensile tests with acoustic emission signal recording were conducted on both notched and unnotched specimens. The detailed analysis of different acoustic emission criteria allowed as to detect each stage of plastic deformation and microstructural damage processes after a long-term operation, and unused carbon steels during quasi-static axial tension testing. The acoustic emission activity, generated in the typical stages of material deformation, was correlated by microscopy observations during the tensile test. The results are to be used as the basis for new algorithms for the assessment of the structural condition of in-service pressure equipment.
Go to article

Abstract

In this paper small punch test (SPT) which is one of miniaturized samples technique, was employed to characterize the mechanical properties of carbon steel P110. The tests were carried out in the range of –175°C to RT. Results obtained for SPT were compared to those calculated for tensile and Charpy impact test. Based on tensile and SPT parameters numerical model was prepared. 8 mm in diameter and 0.8 mm in height (t) discs with and without notch were employed in this research. The specimens had different depth notch (a) in the range of 0.1 to 0.4 mm. It was estimated that α factor for comparison of Tsp and DBTT for carbon steel P110 is 0.55 and the linear relation is DBTT = 0.55TSPT. The numerical model fit with force – deflection curve of SPT. If the factor of notch depth and samples thickness is higher than 0.3 the fracture mode is transformed from ductile to brittle at –150°C.
Go to article

This page uses 'cookies'. Learn more