In the current study, the hot deformation of medium carbon V-Ti micro-alloyed steel was surveyed in the temperature range of 950 to 1150°C and strain rate range of 0.001 to 1 s–1 after preheating up to 1200°C with a compression test. In all cases of hot deformation, dynamic recrystallization took place. The influence of strain rate and deformation temperature on flow stress was analyzed. An increase in the strain rate and decrease in the deformation temperature postponed the dynamic recrystallization and increased the flow stress. The material constants of micro-alloyed steel were calculated based on the constitutive equations and Zener-Hollomon parameters. The activation energy of hot deformation was determined to be 458.75 kJ/mol, which is higher than austenite lattice self-diffusion activation energy. To study the influence of precipitation on dynamic recrystallization, the stress relaxation test was carried out in a temperature range of 950 to 1150°C after preheating up to 1200°C. The results showed no a stress drop while representing the interaction of particles with dynamic recrystallization.
This study investigates the effects of frequency, compression force and Vee angle parameters of High-Frequency Electric Resistance Welding (HF-ERW) process on mechanical properties of API X52 microalloy steel welding joint. Therefore, API X52 microalloy steel sheets having thickness of 8 mm was provided to manufacture pipes with the diameter of 16”. with direct weld seams using the HF-ERW method. During the manufacturing process, frequency values of 150, 200 and 250 kHz, compression forces of 2, 4 and 6 mark and Vee angles of 3°, 5°, and 7° were adopted. After changing the welding parameters, from the welded pipes, tensile and Charpy impact test samples prepared to macroscopically evaluate the weld metal flow and examine the effects of these parameters on mechanical properties of the welded joints. According to the results, it was concluded that frequency of 150 kHz, the compression force of 4 mark and Vee angle of 5° yields best mechanical properties in the HF-ERW joint of API X52 microalloy steel.