The results of studies on the use of modern two cored wires injection method for production of nodular graphite cast iron with use of unique implementation of drum ladle as a treatment/ transport and casting ladle instead vertical treatment ladle was described. The injection of length of Ø 9mm wires, cored: in FeSi + Mg nodulariser mixture and inoculant master alloy is a treatment method which can be used to produce iron melted in coreless induction furnace. This paper describes the results of using this method for possibility production of ductile iron under specific industrial conditions. In this case was taken ductile iron with material designation: EN-GJS-450- 10 Grade according PN-EN 1563:2000. Microstructure of 28 trials was controlled on internally used sample which has been correlated with standard sample before. The paper presents typical metallic matrix and graphite characteristic. Additionally, mechanical properties were checked in one experiment. Because of further possibility treatment temperature reduction only the rough magnesium recovery and cost of this new method are given.
The results of studies on the use of magnesium alloy in modern Tundish for production of vermicular graphite cast irons were described. This paper describes the results of using a low-magnesium ferrosilicon alloy for the production of vermicular graphite cast irons. The paper presents a vermicular (and nodular) graphite in different walled castings. The results of trials have shown that the magnesium Tundish process can produce high quality vermicular graphite irons under the specific industrial conditions of Foundries - Odlewnie Polskie S.A. in Starachowice. In this work describes too preliminary studies on the oxygen state in cast iron and their effect on graphite crystallization.
The results of studies on the use of magnesium alloy in modern Tundish + Cored Wire injection method for production of vermicular graphite cast irons were described. The injection of Mg Cored Wire length is a treatment method which can be used to process iron melted in an electric induction furnace. This paper describes the results of using a high-magnesium ferrosilicon alloy in cored wire for the production of vermicular graphite cast irons at the; Tundish + Cored Wire to be injected methods (PE) for pearlitic-ferritic matrix GJV with about 25 %ferrite content. The results of calculations and experiments have indicated the length of the Cored Wire to be injected basing on the initial sulfur content and weight of the treated melt. The paper presents a microstructure matrix and vermicular graphite in standard sample and different walled castings. The results of numerous trials have shown that the magnesium Tundish + PE Method process can produce high quality vermicular graphite irons under the specific industrial conditions of the above mentioned foundries.
A cast iron is gradient material. This means that depending on the cooling rate it is possible, at the same chemical composition and the physicochemical state of molten metal, to obtain material with a different structure. The connection between the wall thickness of the casting and the speed of its cooling expresses the casting module. Along with the module escalation a cooling rate of the casting is reducing what can cause changes of the microstructure and the increased tendency to the crystallization of distorted graphite forms. Inspections of experimental castings from nodular cast iron with different modules were conducted to the graphite form.
The article presents the results of the research on the influence of the shape of reaction chamber on spheroidisation of cast iron produced with use of the inmold method. The amounts of nodular graphite precipitates in castings produced with the use of different reaction chambers have been compared.
The paper presents the results of abrasive wear resistance tests carried out on high-vanadium cast iron with spheroidal VC carbides. The cast iron of eutectic composition was subjected to spheroidising treatment using magnesium master alloy. The tribological properties were examined for the base cast iron (W), for the cast iron subjected to spheroidising treatment (S) and for the abrasion-resistant steel (SH). Studies have shown that high-vanadium cast iron with both eutectic carbides and spheroidal carbides has the abrasion resistance twice as high as the abrasion-resistant cast steel. The spheroidisation of VC carbides did not change the abrasion resistance compared to the base high-vanadium grade.