Microstructures and mechanical properties of as-cast Al-6.5Mg-1.5Zn-0.5Fe alloys newly alloy-designed for the parts of automobile were investigated in detail. The aluminum (Al) sheets of 4 mm thickness, 30 mm width and 100 mm length were reduced to a thickness of 1mm by multi-pass rolling at ambient temperature and subsequently annealed for 1h at 200~500°C. The as-cast Al sheet was deformed without a formation of so large cracks even at huge rolling reduction of 75%. The recrystallization begun to occur at 250°C, it finished at 350°C. The as-rolled material showed tensile strength of 430 MPa and tensile elongation of 4.7%, however the specimen after annealing at 500°C showed the strength of 305 MPa and the elongation of 32%. The fraction of high angle grain boundaries above 15 degree increased greatly after annealing at high temperatures. These characteristics of the specimens after annealing were discussed in detail.
Przejdź do artykułu

Ta strona wykorzystuje pliki 'cookies'. Więcej informacji