Directionally solidified sample of Fe-Fe3C eutectic alloy were produced under an argon atmosphere in a vacuum Bridgman-type furnace to study the eutectic growth with v = 167 μm/s pulling rate and constant temperature gradient G = 33.5 K/mm. Since how the growth texture of eutectic cementite is related to its growth morphology remains unclear, the current study aims to examine this relationship. The technique such as X-ray diffraction, have been used for the crystallographic analysis of carbide particles in white cast irons.
Directional solidification of ledeburite was realised out using a Bridgman’s device. The growth rate for movement sample v=83.3 μm/s was used. In one sample the solidification front was freezing. The value of temperature gradient in liquid at the solidification front was determined. Interfacial distance λ on the samples was measured with NIS-Elements application for image analysis.
Directional solidification of the Fe - 4,3 wt % C alloy was performed with the pulling rate equal to v=83 μm/s. Sample was frozen during solidification to reveal the shape of the solid/liquid interface. Structures eutectic pyramid and spherolitic eutectic were observed. The solidification front of ledeburite eutectic was revealed. The leading phase was identified and defined.