In this research reactive powder concrete (RPC) was prepared using sand from North Sinai. The mechanical properties of locally cast RPC were investigated and evaluated by studying the effects of using different cement and silica fume contents and new steel fi bers’ aspect ratios as reinforce-ment for RPC. Specimens’ preparation, curing regimes and testing procedures to evaluate the com-pressive strength, the modulus of elasticity, the indirect tensile strength and the fl exural strength were discussed. A compressive strength of 154.5 MPa, indirect tensile strength of 11.98 MPa, mod-ulus of elasticity of 45.1 GPa and fl exural strength of 30.26 MPa have been achieved for reinforced RPC contains 800 kg/m³ cement content and silica fume content 30% of cement weight. The test results showed some improvements by increasing cement and silica fume contentsas well as adding steel fi bers on the compressive strength, modulus of elasticity and indirect tensile strength.
Go to article

Abstract

The paper deals with the properties and microstructure of Reactive Powder Concrete (RPC), which was developed at Cracow University of Technology. The influence of three different curing conditions: water (W), steam (S) and autoclave (A) and also steel fibres content on selected properties of RPC was analyzed. The composite characterized by w/s ratio equal to 0.20 and silica fume to cement ratio 20%, depending on curing conditions and fibres content, obtained compressive strength was in the range from 200 to 315 MPa, while modulus of elasticity determined during compression was about 50 GPa. During three-point bending test load-deflection curves were registered. Base on aforementioned measurements following parameters were calculated: flexural strength, stress at limit of proportionality (LOP), stress at modulus of rapture (MOR), work of fracture (WF), and toughness indices I₅, I₁₀ and I₂₀. Both amount of steel fibres and curing conditions influence the deflection of RPC during bending.
Go to article

This page uses 'cookies'. Learn more